Glossary entry (derived from question below)
English term or phrase:
flattening & flaring
Polish translation:
testy wykrywania pęknięc w czasie spłaszczania i wywijania
Added to glossary by
ZenonStyczyrz
Feb 28, 2005 20:35
19 yrs ago
13 viewers *
English term
flattening & flaring
English to Polish
Other
Metallurgy / Casting
hutnictwo
tekst o rurach bez szwu ze stali nierdzewnej
microstructure tests: flattening - 1-2 stage: acceptable
chodzi mi po głowie "prostowanie", "równanie" i "spłaszczanie"
flaring - acceptable
W słowniku technicznym znalazłem "podnoszenie temperatury kąpieli metalowej aż do zapalenia się gazów nad powierzchnią kąpieli" oraz definicja druga: "rozszerzenie, np. rury u wylotu"
tekst o rurach bez szwu ze stali nierdzewnej
microstructure tests: flattening - 1-2 stage: acceptable
chodzi mi po głowie "prostowanie", "równanie" i "spłaszczanie"
flaring - acceptable
W słowniku technicznym znalazłem "podnoszenie temperatury kąpieli metalowej aż do zapalenia się gazów nad powierzchnią kąpieli" oraz definicja druga: "rozszerzenie, np. rury u wylotu"
Proposed translations
(Polish)
4 | testy wykrywania pęknięc w czasie spłaszczania i wywijania | A.G. |
Proposed translations
50 mins
Selected
testy wykrywania pęknięc w czasie spłaszczania i wywijania
Flaring test
The flaring test serves the verification of the formability of tubes by expanding on a mandrel up to a determined amount without formation of incipient cracks.
Flattening test on tubes
The flattening test on tubes is mainly utilized for the verification of macroscopic external and internal defects as well as the assessment of deformability. During flattening of the tubes cross section up to a certain limit value, no incipient cracks may occur and no internal and external defects may become visible.
The flaring test serves the verification of the formability of tubes by expanding on a mandrel up to a determined amount without formation of incipient cracks.
Flattening test on tubes
The flattening test on tubes is mainly utilized for the verification of macroscopic external and internal defects as well as the assessment of deformability. During flattening of the tubes cross section up to a certain limit value, no incipient cracks may occur and no internal and external defects may become visible.