Glossary entry (derived from question below)
English term or phrase:
mold shrinkage
Polish translation:
skurcz formy
- The asker opted for community grading. The question was closed on 2013-11-24 10:54:23 based on peer agreement (or, if there were too few peer comments, asker preference.)
Nov 20, 2013 13:38
10 yrs ago
7 viewers *
English term
mold shrinkage
English to Polish
Tech/Engineering
Materials (Plastics, Ceramics, etc.)
Z charakterystyki technicznej produktu (poliwęglan). Właściwości fizyczne:
Mold Shrinkage on Tensile Bar, flow (2) - 0,2-0,6% wg normy ASTM D 955
Mold Shrinkage on Tensile Bar, flow (2) - 0,2-0,6% wg normy ASTM D 955
Proposed translations
3 hrs
Frank Szmulowicz, Ph. D.
United States
United States
Native in English
&
Polish
Specializes in field
United States
On time, on target, on budget.
Native in: English 
, Polish
Works in: Polish to English, English to Polish, Russian to Polish, and 1 more.
Related KudoZ points
:
230
Selected
skurcz formy
Shrinkage = skurcz
Mold = forma albo inne wyrażenie
Wprawdzie wraz ze wzrostem temperatury formy zwiększa się wartość skurczu całkowitego, ale udział skurczu wtórnego jest wtedy tak niewielki, że można uzyskaćwystarczającą stabilność wymiarową wypraski.
--------------------------------------------------
Note added at 5 hrs (2013-11-20 19:15:07 GMT)
--------------------------------------------------
Sugestia od A. G.: skurcz wyprasek
Wpływ parametrów wtryskiwania na skurcz wyprasek
http://www.prz.rzeszow.pl/chemia/ztts/Wtrysk_amorf_kryst_nap...
doświadczalne został określony związek między skurczem wypraski
http://www.pnt.pollub.pl/pdf/nr7/23.pdf
itp
Mold = forma albo inne wyrażenie
Wprawdzie wraz ze wzrostem temperatury formy zwiększa się wartość skurczu całkowitego, ale udział skurczu wtórnego jest wtedy tak niewielki, że można uzyskaćwystarczającą stabilność wymiarową wypraski.
--------------------------------------------------
Note added at 5 hrs (2013-11-20 19:15:07 GMT)
--------------------------------------------------
Sugestia od A. G.: skurcz wyprasek
Wpływ parametrów wtryskiwania na skurcz wyprasek
http://www.prz.rzeszow.pl/chemia/ztts/Wtrysk_amorf_kryst_nap...
doświadczalne został określony związek między skurczem wypraski
http://www.pnt.pollub.pl/pdf/nr7/23.pdf
itp
Reference:
Peer comment(s):
| neutral |
A.G.
: formy czy wypraski?
1 hr
|
|
Dobre pytanie, A. G.. Widziałem wypraski w tym kontekście, dlatego sugerowałem inne wyrażenia. Dziękuję.
|
|
| neutral |
IRA100
: forma się nie kurczy"))))
2 hrs
|
|
Thanks, IRA100. What better name do you have for the result of molding? The result of molding is also called a mold. Skurcz is the process.
|
2 KudoZ points awarded for this answer.
Comment: "Ostatecznie napisałam "skurcz przetwórczy", ale ta odpowiedź mnie naprowadziła na dobry trop. Dziękuję"
1 hr
odkształcenie
odkształcenie w trakcie próby rozciągania
Note from asker:
| Wyżej były już takie dane jak: Wytrzymałość na rozciąganie na granicy plastyczności; Wydłużenie przy rozciąganiu; Wydłużenie do zerwania; Wytrzymałość na zginanie. Więc myślę, że tu chodzi o coś bardziej konkretnego. |
7 hrs
Andrzej Mierzejewski
Poland
Poland
Native in Polish
Specializes in field
Poland
M.Sc. Engineer (Mechanics)
Native in: Polish
Works in: Polish to English, English to Polish, German to Polish, and 3 more.
Related KudoZ points
:
115
English term (edited):
mold shrinkage on tensile bar
skurcz wypraski mierzony na listwie (próbce do rozciągania)
Mold shrinkage is the shrinkage of the polymer as it cools after the molding process. It is typically used to properly machine injection molds so that final part dimensions are as desired.
http://www.ptli.com/testlopedia/tests/Mold_Shrinkage-D955.as...
Most mold makers and molders face the problem of mold shrinkage of polypropylene (PP) and polyethylene (PE).
http://www.lyondellbasell.com/techlit/techlit/Tech Topics/Ge...
Problem bierze się z tego, że i forma, i produkt są określane wyrazem "mold/mould.
Nie wiem dokładnie, jak przetłumaczyć "on tensile bar", więc pewność niecałkowita.
http://www.ptli.com/testlopedia/tests/Mold_Shrinkage-D955.as...
Most mold makers and molders face the problem of mold shrinkage of polypropylene (PP) and polyethylene (PE).
http://www.lyondellbasell.com/techlit/techlit/Tech Topics/Ge...
Problem bierze się z tego, że i forma, i produkt są określane wyrazem "mold/mould.
Nie wiem dokładnie, jak przetłumaczyć "on tensile bar", więc pewność niecałkowita.
22 hrs
Frank Szmulowicz, Ph. D.
United States
United States
Native in English
&
Polish
Specializes in field
United States
On time, on target, on budget.
Native in: English , Polish
Works in: Polish to English, English to Polish, Russian to Polish, and 1 more.
Related KudoZ points
:
230
skurcz wypraski mierzony na próbce do próby rozciągania
tensile bar = próbka do próby rozciągania
z poprzedniej odpowiedzi
shrinkage = skurcz
wypraski = zobacz moją poprzednią odpowiedż, sugestia A. G.
Wpływ parametrów wtryskiwania na skurcz wyprasek
Dodaję tensile bar = próbka do próby rozciągania ze słowniczka technicznego
z poprzedniej odpowiedzi
shrinkage = skurcz
wypraski = zobacz moją poprzednią odpowiedż, sugestia A. G.
Wpływ parametrów wtryskiwania na skurcz wyprasek
Dodaję tensile bar = próbka do próby rozciągania ze słowniczka technicznego
Discussion
Test Procedure:
The length or diameter of the cavity is measured depending on shape of mold. Test specimens are molded under specified conditions. The parts cool and after 48 hours, the molded parts are measured and the shrinkage is calculated.